Sinomaco polymer cement waterproof coating

Short Description:

Sinomaco Polymer Cement Waterproof Coating (JS coating) is made of high-quality emulsion as acrylate, ethylene-acetate, vinyl ester produced which was produced by BASF in Germany as the main raw material. This coating is a two-component waterproof coating which is produced by mixing the synthetic organic liquid material and inorganic powder material in scientific formula and production process. Product Feature 1. Fast curing, good elasticity, and good water resistance after the coating is d...


  • Product: Polymer cement waterproof coating
  • Reference dosage: 2.1kg-2.4kg/㎡/mm
  • Application: Suitable for toilet, floor, wall, shower room, baclcony waterproofing; hydropower projects, dams, tunnels, bridges, ponds, water towers, purification pools, reservoirs, swimming pools and other waterproof projects with high permeability and pressure resistance
  • Product Detail

    Product Tags

    Sinomaco Polymer Cement Waterproof Coating (JS coating) is made of high-quality emulsion as acrylate, ethylene-acetate, vinyl ester produced which was produced by BASF in Germany as the main raw material. This coating is a two-component waterproof coating which is produced by mixing the synthetic organic liquid material and inorganic powder material in scientific formula and production process.

    Product Feature

    1. Fast curing, good elasticity, and good water resistance after the coating is dry, and it can be directly applied on the wet and dry base surface.

    2. Cold applied construction which is easy to operate can reduce the construction period and makes it easy to be maintained.Environmentally friendly, cause the coating is non-toxic, odorless, and non-polluting.

    3. Excellent performance in strong adhesion, toughness, water resistance, weather resistance, anti-corrosion, aging resistance, durability and strong adhesion to the base.

    4. Various king of colors are available for customers demand which makes a beautiful appearance.

    Application Scope  

    1. Suitable for hydropower projects, dams, tunnels, bridges, ponds, water towers, purification pools, reservoirs, swimming pools and other waterproof projects with high permeability and pressure resistance.

    2. It is suitable for filling leaks and cracks by mixing this product with water, cement, etc. to form a paste, and then fills, repairs, and plugs leaks through the gaps and cracks in the through-holes.

    3. According to different working demands, different kind of models (Type I, Type II, Type III) can be choose. Type I is suitable for floor base with large amount of activity, Type II and Type III are suitable for floor base with smaller activity.

     Working advice

    1. Add as suitable water as possible when painting to avoid flowing or dripping.

    2. Do not construct in the rain day so the film formation can not be affected. Never allow rain and people to walk before the waterproof layer has cured.

    3. The thickness of the coating should be uniform to avoid delamination, cracking, bubbles, wrinkles, or pile-ups.

    Transportation & storage

    1. Tightly sealed and placed it in a clean, ventilated and dry warehouse to avoid direct sunlight. If the storage period exceeds, it can be re-inspected to ensure its qualification.

    2. Be ensure that the packaging is intact, and keep the coating away from collision, extrusion, rain, and freezing during transportation.

    Performance Test Report

    Performance Test Report

    S/N

    Test Item

    Technical Index

    1

    Solid content

    ≥70  %

    ≥70  %

    ≥70  %

    2

    Tensile Strength

    Without treatment

    ≥1.2 Mpa

    ≥1.8 Mpa

    ≥1.8 Mpa

    Retention rate after heat treatment

    ≥80%

    ≥80%

    ≥80%

    Retention rate after alkali treatment

    ≥60%

    ≥70%

    ≥70%

    Retention rate after water soaking treatment

    ≥60%

    ≥70%

    ≥70%

    Retention rate after UV treatment

    ≥80%

    -

    -

    3

    Elongation rate at break

    Without treatment

    ≥200%

    ≥80%

    ≥30%

    Retention rate after heat treatment

    ≥150%

    ≥65%

    ≥20%

    Retention rate after alkali treatment

    ≥150%

    ≥65%

    ≥20%

    Retention rate after water soaking treatment

    ≥150%

    ≥65%

    ≥20%

    Retention rate after UV treatment

    ≥150%

    -

    -

    4

    Low temperature flexibility ø10mm

    -10℃,No crack

    -

    -

    5

    Bond strength

    Without treatment

    ≥0.5Mpa

    ≥0.7Mpa

    ≥1.0Mpa

    Moisture base

    ≥0.5Mpa

    ≥0.7Mpa

    ≥1.0Mpa

    Alkaline treatment

    ≥0.5Mpa

    ≥0.7Mpa

    ≥1.0Mpa

    Water soaking treatment

    ≥0.5Mpa

    ≥0.7Mpa

    ≥1.0Mpa

    6

    Watertightness 0.3Mpa,30min

    Impermeable

    Impermeable

    Impermeable

    7

    Impermeability (mortar surface)

    -

    ≥0.6Mpa

    ≥0.8Mpa

    Note: Production Standard: GB/T23445-2009