Elastomer Silicone Waterproof Coating

Short Description:

Silicone Based Waterproof Coating also called organic silicon based waterproof coating is a water-based environmentally friendly waterproof coating made of silicone rubber latex and its nano composite emulsion as the main base material, mixed with inorganic fillers and various additives. Main feature 1. The overall film-forming property is good. After the coating film is cured, it will form a continuous, uniform and integrated rubber-like elastomer, so the waterproof layer made has no overla...


Product Detail

Product Tags

Silicone Based Waterproof Coating also called organic silicon based waterproof coating is a water-based environmentally friendly waterproof coating made of silicone rubber latex and its nano composite emulsion as the main base material, mixed with inorganic fillers and various additives.

silicone coating S20 (1)

Main feature

1. The overall film-forming property is good. After the coating film is cured, it will form a continuous, uniform and integrated rubber-like elastomer, so the waterproof layer made has no overlap joints, which is more suitable for the construction of special-shaped parts.

2. It has good elongation and good tensile strength.

3. Single component, water emulsion type and can be made into color coating.

4. Convenient construction. It can be constructed by scraping, painting and brushing. It does not have strict requirements on the humidity of the base layer and can be constructed on wet surfaces. Cold construction is especially advantageous for construction sites where open flames are prohibited and complex shapes are prohibited.

5. Green and environmental protection, non-toxic and tasteless, convenient and safe to use.

Scope of application

It is used for waterproofing, anti-seepage, moisture-proof and gas-proofing of new and old roofs, roofs, basements, bathrooms, swimming pools, warehouses, and bridge projects. Its life span can reach 30 years.

The new color silicone rubber waterproof coating has good adhesion and permeability to cement mortar, concrete matrix, wood, ceramics, glass and other building materials. Practice has proved that when it is applied to mortar and concrete matrix, it can penetrate 0.3 mm, and firmly hold, it is especially suitable for pasting or plastering the outer surface after painting, especially for basement, bathroom, toilet leakage repair, which is unmatched by other waterproof materials .

In addition, this product also solves the waterproof and sun protection problems of aluminum alloy balconies and window rain covers.

Construction method

1. Grassroots treatment: the surface of the grassroots is required to be flat, and no unevenness and sanding are allowed.

2. Joint treatment: If the roof has cracks above 3mm, the sealing material should be filled, and then the coating should be applied.

3. Scratch coating: Rolling, scraping, painting or brushing can be used for construction. Generally, 3-4 coats are applied, and the reference amount for each coat is 0.8-1.0 kg/m2.

4. The total thickness of the coating film is above 1.5mm, and the interval between each coating is 2-12h (depending on the weather conditions). 1-2 layers of glass fiber cloth or other carcass materials can be added in the middle of the coating.

silicone coating S20 (3)

Dosage recommended

Generally 1.5-2 kg/m²

Packaging, storage and transportation

This product is packaged in airtight barrels or pails, the storage temperature should not be lower than 0, and the storage period is more than nine months.

This product is non-toxic, non-flammable, non-corrosive, and can be transported as ordinary goods.

Note:

1. It is not suitable for construction when the temperature is lower than 5.

2. Construction is prohibited on rainy and snowy days.

Technical data sheet

S/N

Test item

Value

1

Appearance

Fine stable liquid

2

Tensile strength

2.0Mpa

3

Elongation at break

310%

4

Low temperature flexibility -10

No crack and break

5

Watertightness (0.3Mpa, 30Min)

Impermeable

6

Solid content

70%

7

Surface drying time

0.4h

8

Solid cure time

0.5h

Result: Qualified