APP torch applied bitumen waterproofing membrane

Short Description:

Sinomaco Plastomer APP/ APAO/ APO Modified Bitumen Waterproofing Membrane is manufactured by using advanced Germany technology and direct mixing process. Select APP (Atactic Polypropylene) or APAO, APO (polyolefin polymer) modified asphalt as dipping material, reinforced with polyester felt, glass fiber felt and glass fiber reinforced polyester felt, surface covered with fine sand, mineral grain (sheet) material , PE film, refined by advanced technology plastic modified bitumen waterproof mem...


  • Product Name:: APP/APO APAO Modified Bitumen Membrane
  • Single roll Length: 8/10/15m
  • Width: 1m
  • Thickness: 2/3/4/5mm
  • Product Detail

    Product Tags

    Sinomaco Plastomer APP/ APAO/ APO Modified Bitumen Waterproofing Membrane is manufactured by using advanced Germany technology and direct mixing process. Select APP (Atactic Polypropylene) or APAO, APO (polyolefin polymer) modified asphalt as dipping material, reinforced with polyester felt, glass fiber felt and glass fiber reinforced polyester felt, surface covered with fine sand, mineral grain (sheet) material , PE film, refined by advanced technology plastic modified bitumen waterproof membrane.

     

    Product Feature

    1. Good elasticity, high tensile strength and elongation, good high temperature flexibility, good wear resistance.

    2. Excellent water impermeability and temperature adaptability.  APP is suitable for building waterproofing in lower temperature environments.

    3. Good corrosion resistance and aging resistance, anti-puncture resistance, mildew resistance, impact resistance, pressure resistance, long service life.

    4. Easy to operate and maintain, and ensure the construction quality.

    5. Specially designed for hot asphalt or heat welding(with burn-off polyethylene)applications. heat welding lap joints are durable, reliable, and tight.

     

    Basic Specification

    Reinforced Layer

    Thickness

    (mm)

    Width

    (mm)

    Cover Material

    Cover Material

    (heat welding side)

    Polyester felt (PY)

    3 / 4 / 5

    1000 mm

    Polyethylene (PE)

    Fine Sand (S)

    Mineral aggregate (M)

    Polyethylene (PE)

    Fiberglass felt (G)

    3 / 4

    Fiberglass Polyester felt

    (PYG)

    5

     

    Application Scope

    1. Suitable for waterproofing and moisture proofing of roofs, basements and industrial cold storage as well as civil building structures.

    2. Waterproofing for water conservancy projects, swimming pools, bridge decks, subways, tunnels, sewage treatment plants, landfills, etc.

    3. It can also be used for anti-corrosion and various moisture-proof interior packaging materials of underground pipelines.

    Transportation & storage

    1. There should be a dedicated warehouse stacking and the warehouse must be ventilated to avoid light exposure, non-fire sources, and fire prevention.

    2. When stacking in temporary warehouses on the construction site, coverings must be covered to avoid sun and rain. When transporting, the membranes should be stacked tightly and the membranes cannot be stacked on each other to prevent the sheet from tilting or lateral pressure. The storage temperature should be not higher than 50°C, the storage period is one year from the date of production, and it can still be used if it is qualified.

    Working Advices

    If there is any snow, water or frost on the ground of the operation, must stop construct. If it is necessary to work under negative temperature, measures should be taken to ensure that the waterproof layer after laying is not cracked or sticky. During the construction, the air needs to be squeezed by hand to avoid bulging. When handling, take it upright and place it upright. The height must not exceed two layers. Prevent tilting or lateral pressure. Do not drop it and avoid damage.

     

    Performance Test Report

    Test Report (Execution Standard: GB18243-2008)

     S/N

     Item

    Index

    PY

    G

    PY

    G

    PYG

    1

    Soluble content

    3㎜

    ≥ 2100 g/㎡

    4㎜

    ≥ 2900 g/㎡

    5㎜

    ≥ 3500 g/㎡

    Test results

    -

    Reinforced layer Nonflammable

    -

    Reinforced layer Nonflammable

    -

    2

    Heat resistance

    Test results

    110℃

    130℃

    ≤ 2㎜

    No flow, no dripping

    3

    Low temperature flexibility

    -7℃

    -15℃

    No crack

    4

    Impermeable (30min)

    0.3Mpa

    0.2Mpa

    0.3Mpa

    5

    Tension

    Maximum peak tension

    ≥500N/50mm

    ≥360N/50mm

    ≥800N/50mm

    ≥500N/50mm

    ≥900N/50mm

    Sub peak tension

    -

    -

    -

    -

    ≥800 N/50mm

    Results

    During the tensile process, there is no cracking of the membrane upper cover layer or the separation of the reinforced layer in the middle of the test sample.

    6

    Elongation rate

    Maximum peak elongation

    ≥25%

    -

    ≥40%

    -

    -

    Second peak elongation

    -

    -

    ≥15%

    7

    Increased quality after soaking

    PE/S

    ≤1.0%

    M

    ≤2.0%

    8

    Thermal aging

    Rally retention rate

    ≥90%

    Elongation retention rate

    ≥80%

    Low temperature flexibility

    -2℃

    -10℃

    No crack

    Size change rate

    ≤0.7%

    -

    ≤0.7%

    -

    ≤0.3%

    Loss of quality

    ≤1.0%

    9

    Joint peel strength

    ≥1.0 N/㎜

    Nail tear strength

    -

    ≥300 N

    Mineral pellet adhesion

    ≤2.0 g

    The thickness of Bitumen cover layer on the downward covered surface of the membrane

    ≥1.0㎜

    10

    Artificial weather accelerated aging

    Appearance

    No sliding, flowing, dripping

    Rally retention rate

    ≥80%

    Low temperature flexibility

    -2 ℃

    -10 ℃

    No crack

    A. only suitable for single layer membrane in mechanical fixed construction.

    B. only applicable to coils on the surface of mineral pellets.

    C. only for hot melt construction.